EuF₃/螺旋碳微米纤维(HCFs)复合结构的制备和发光性能

^1,2

^1,2*

作者信息 +

Preparation and luminescence property of EuF₃/HCFs with composite structure

Wang Wei¹, Zhang Zhihua¹, Cao Qiyi¹, Zhu Shuyuan¹, Wen Yadong¹, Wang Gang^1,2, Wang Zhijun^1,2, Sun Yufeng^1,2, Tao Feng^1,2

Author information +

文章历史 +

Received
2020-03-11
Issue Date	Revised Date
2021-08-19	2020-03-11

PDF

摘要

以茶叶体内的螺旋导管为模板,通过水热处理制备了氟化铕(EuF₃)/螺旋碳微米纤维(HCFs)复合结构。通过X射线衍射(XRD)、场扫描电子显微镜(SEM)和红外光谱(FT-IR)等对样品的物相、结构和形貌进行了表征。结果表明,水热碳化后,生物体内的螺旋导管结构得到了完美保留。室温下光致发射光谱和荧光寿命测试结果显示,在317nm激发波长下,Eu³⁺与HCFs间发生能量转移现象,使HCFs在紫外光区354nm处发射明显增强,这表明Eu³⁺/HCFs复合材料是一种新型的紫外发射材料。

Abstract

EuF₃/helical carbon microfibers (HCFs) with composite structure was prepared by hydrothermal method using spiral vessels (SVs) in tea-leaves as template.The phase,structure and morphology of the samples were characterized by X-ray diffraction (XRD),field emission scanning electron microscopy (SEM) and infrared spectroscopy.The results showed that the helical structure was perfectly preserved after hydrothermal carbonization.The results of photoluminescence spectra and fluorescence lifetime at room temperature showed that the energy transfer between Eu³⁺ and HCFs occurred at the excitation wavelength of 317nm,which significantly enhanced the emission of helical carbon micron fiber at 354nm in the ultraviolet region,indicating that Eu³⁺/HCFs was a new type of ultraviolet emission material.

关键词

Eu³⁺ / 螺旋碳纤维 / 水热合成 / 复合结构 / 紫外发射

Key words

Eu³⁺ / helical carbon fiber / hydrothermal synthesis / composite structure / ultraviolet emission

引用本文

引用格式 ▾

EuF₃/螺旋碳微米纤维(HCFs)复合结构的制备和发光性能[J]. 化工新型材料, 2021, 49(7): 73-77 DOI:10.19817/j.cnki.issn 1006-3536.2021.07.017

登录浏览全文

4963

注册一个新账户忘记密码

参考文献

原文顺序 | 出版日期 | 本文引用

[1] Kozak O,Sudolska M,Pramanik G,et al.Photoluminescent carbon nanostructures[J].Chem Mat,2016,28(12):4085-4128.
[2] Gupta B K,Shanker V,Arora M,et al.Photoluminescence and electron paramagnetic resonance studies of springlike carbon nanofibers[J].Appl Phys Lett,2009,95(7):3.
[3] Deeney C,Wang S X,Belhout S A,et al.Templated microwave synthesis of luminescent carbon nanofibers[J].RSC Adv,2018,8(23):12907-12917.
[4] Hikita M,Cao L,Lafdi K.Optical properties of carbon microcoils[J].Appl Phys Lett,2014,104(4):4.
[5] Chen Y,Xu J F,Liu B T,et al.Enhanced photoluminescence properties of carbon dots by doping with europium[J].J Nanosci Nanotechnol,2016,16(4):3735-3738.
[6] Wen J F,Zhang Y,Tang N J,et al.Synthesis,photoluminescence,and magnetic properties of nitrogen-doping helical carbon nanotubes[J].J Phys Chem C,2011,115(25):12329-12334.
[7] 王莹,李勇,朱靖,等.氧化石墨烯表面稀土改性机理[J].材料工程,2018,46(5):29-35.
[8] 王福,李艾,郝玉翠,等.氧化石墨烯/氧化铕复合材料粉体的光催化性能研究[J].粉末冶金工业,2016,26(2):8-11.
[9] 杨辉煌.纳米氧化钌及其与氮掺杂碳纳米管复合材料的制备与性能研究[D].北京:北京化工大学,2017.
[10] 赵永霞.石墨烯/稀土氧化物的制备及其性能研究[D].兰州:西北师范大学,2012.
[11] 吴江.碳量子点增强稀土离子荧光的研究[D].南京:东南大学,2016.
[12] Raghubanshi H,Dikio E D,Naidoo E B.The properties and applications of helical carbon fibers and related materials:a review[J].J Ind and Eng Chem,2016,44:23-42.
[13] Chen X Q,Zhang S L,Dikin D A,et al.Mechanics of a carbon nanocoil[J].Nano Lett,2003,3(9):1299-1304.
[14] Raghubanshi H,Dikio E D.Synthesis of helical carbon fibers and related materials:a review on the past and recent developments[J].Nanomaterials,2015,5(2):937-968.
[15] Tang L B,Ji R B,Cao X K,et al.Deep ultraviolet photoluminescence of water-soluble self-passivated graphene quantum dots[J].ACS Nano,2012,6(6):5102-5110.
[16] Lin J,Feng C C,He X,et al.Europium(Ⅲ) organic complexes in porous boron nitride microfibers:efficient hybrid luminescent material[J].Scientific Reports,2016,6:7.
[17] Gray D G.Isolation and handedness of helical coiled cellulosic thickenings from plant petiole tracheary elements[J].Cellulose,2014,21(5):3181-3191.
[18] Yang Q M,Duan J L,Yang W,et al.Nitrogen-doped carbon quantum dots from biomass via simple one-pot method and exploration of their application[J].Appl Surf Sci,2018,434:1079-1085.
[19] Huo Q Y,Tu W X,Guo L.Enhanced photoluminescence property and broad color emission of ZnGa₂O₄ phosphor due to the synergistic role of Eu³⁺ and carbon dots[J].Opt Mater,2017,72:305-312.
[20] Pan D Y,Zhang J C,Li Z,et al.Hydrothermal route for cutting graphene sheets into blue-luminescent graphene quantum dots[J].Adv Mater,2010,22(6):734-738.